Surface Fluorinated Microsized-TiO۲ for Formulation of Self-Cleaning Cement

The use of nanosized-Titanium dioxide (n-TiO۲) for the formulation of self-cleaning cement has the associated drawbacks of nano-toxicity, higher cost, and agglomeration in the cementitious material. These drawbacks can be avoided by the replacement of  n-TiO۲ with microsized TiO۲ (m-TiO۲). However, m-TiO۲ is less photocatalytically active as compared to n-TiO۲ . Therefore, in the present work, surface fluorination of  m-TiO۲  has been studied to enhance its photocatalytic activity for the formulation of self-cleaning white cement. The commercially available m-TiO۲ (average size ۴۰ μm) was surface fluorinated using aqueous solutions of different molar concentrations of NaF (sodium fluoride) such as ۱۰, ۵۰, and ۱۰۰ mmol/dm۳. The surface fluorinated m-TiO۲ was analyzed using Diffuse Reflectance (DRS) Spectroscopy, PhotoLuminescence (PL) spectroscopy, and X-Ray diffraction (XRD) analysis to observe the improvement in the physiochemical properties and photocatalytic characteristics. Further, the surface fluorinated m-TiO۲ along with calcined dolomite was utilized for the formulation of self-cleaning white cement. The hence prepared self-cleaning cement was cast into cement slabs, which were then characterized by Diffuse Reflectance Spectroscopy (DRS) and Energy Dispersive Spectroscopy (EDS). The self-cleaning ability and photocatalytic activity of the as-prepared cement slabs were evaluated through Rhodamine B (RhB) degradation test. It has been found that the use m-TiO۲, which was surface fluorinated using ۱۰ mmol/dm۳ solution of NaF, remarkably enhanced the photocatalytic performance of the self-cleaning cement.

کلیدواژه ها:

Titanium dioxide ، Self-cleaning cement ، photocatalytic activity ، Photocatalysis ، Surface fluorination ، White cement