Mineralogical and Physicochemical Characterization of Enugu Iva-Pottery Silica-Rich Deposit for Ceramics Applications

The exploration of indigenous raw materials that are pure and simple to process for ceramics is a scalable option for locally-made ceramics products. This study involves the characterization of unexplored silica-rich sand deposits at Iva-pottery, Enugu North local government area in Enugu state Nigeria for their ceramic industrial potential. The physicochemical properties of Iva-pottery silica-rich sand were determined. The crystalline phase components and elemental compositions of the oxide were investigated with an X-ray diffractometer and an X-ray fluorescence spectrophotometer respectively. The silica was used in ceramics composition as a filler and glaze formulation as glass former.  The results obtained showed mainly a siliceous crystalline phase with a minor amorphous phase and contains ۷۴.۵۵% SiO۲, ۱۳.۰۲% Al۲O۳, and ۰.۵۵% Fe. The grain size in the raw form is in the range of ۰.۱۸ mm to ۰.۰۷۵ mm (۱۰۰ mesh to + ۲۰۰ mesh range) without involving ceramic raw materials processing equipment such as a ball mill as well as a high percentage of alumina (۱۳.۰۲) contents as compared to conventional silica with alumina ۰.۰۲% to ۰.۵% range. The high alumina that forms mullite at sintering temperature brings about a low thermal coefficient and hence, suitable chemical stability and resistance to thermal shock.  These rare qualities make the Iva-pottery silica-rich sand an emergent material suitable for glaze formulation and filler in ceramic bodies. Thus, it is recommended that the Iva-pottery silica-rich sand deposits in their raw form be exploited for the formulation of varied glaze temperature ranges and also for the refractory industry. Iva-pottery silica-rich deposits in their raw form, do not meet the requirements of high tech- ceramics applications.

کلیدواژه ها:

ceramic application ، Enugu ، Iva-pottery silica sand ، Minerals ، X-ray Diffractometer