Silver Recovery from Printed Circuit Based Using Deep Eutectic Solvent-Glyceline (DES-Glyceline)

Silver is an element with the highest thermal and electrical conductivity, making it ideal for electrical applications. One of the most commonly consumed electronic wastes containing silver is Printed Circuit Boards (PCBs). To reduce the amount of PCB waste and increase the availability of silver, an environmentally friendly solvent called Deep Eutectic Solvent (DES) is proposed to extract silver from PCB waste. This study aims to synthesize DES-glyceline and investigate the behavior and effectiveness of silver extraction using this DES glyceline. The optimum mole ratio of choline chloride and glycerol to synthesize DES was ۱:۲. The density of DES-glyceline was measured by a pycnometer, about ۱.۱۳۷۸ g/L. The FT-IR spectra showed a broadening peak of the O-H band and its shifting from ۳۲۷۳ cm-۱ in glycerol to ۳۱۲۴ cm-۱ in DES-glyceline. The NMR characterization demonstrated the deshielding effect of O-H proton in glycerol, from ۳.۴۴ ppm to ۴.۶۳ ppm and ۵.۱۹ ppm. Both results indicate the formation of hydrogen bonds attributed to DES formation. The success of silver extraction by DES-glyceline was proven by cyclic voltammetry, resulting in an anodic peak at ۰.۱۳۲ V and a cathodic peak at -۰.۰۳۷ V. XRF characterization showed that the silver concentration contained in the initial PCB sample was ۱۷۸.۵۹ ppm. The recovery optimum condition for silver from PCB extraction was at the temperature of ۱۲۰°C and at the time of ۱۶ hours with a leaching percentage of almost ۸۵%. This environmentally friendly, low-cost, low toxicity, and high biodegradability DES-glyceline shows tremendous promise for efficiently recovering silver from PCB e-waste.

کلیدواژه ها:

Silver recovery ، DES glyceline ، Leaching ، Cyclic voltammetry ، Metal recovery ، deep eutectic solvent