The Hydration Products of a Refractory Calcium Aluminate Cement at Low Temperatures

Calcium aluminates (CA) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements.  The anhydrous phases of this kind of cements are CA, CA۲ and traces of C۱۲A۷ and alpha-alumina. The major hydraulic phase in all of the CA cements including ciment fondue is CA. Once hydrated, it starts to form the hexagonal crystals of CAH۱۰ and C۲AH۸ that depending on the time and temperature of hydration converts to the cubic crystals of C۳AH۶ and AH۳. The nature of the calcium aluminate hydrates, their morphology and the way in which they are broken down, play an important roles in determining the properties of fired cement.  For this reason a series of investigations has been conducted on the hydration reactions of Secar ۷۱, a commercial cement which can completely represents this type of cements, and hydration products were characterized by DTA, DSC, XRD and SEM. At ۱۲ oC, the only hydration products were a gel phase, CAH۱۰ and gibbsite, while the same hydrates were still predominant phases, C۴ACH۱۱ also formed as a result of carbonation of the pastes.

کلیدواژه ها:

Calcium aluminate cement (CAC) ، Hydration reactions ، CAH۱۰ ، C۲AH۸ ، C۳AH۶ ، AH۳