On the Magnetic Properties of High Entropy Intermetallic Compounds

High entropy intermetallic compounds (HEICs) are an interesting class of materials combining the properties of multicomponent solid solutions and the ordered superlattices in a single material. In this work, microstructural and magnetic properties of (CoCuFeMnNi)Al, (CoCuFeMnNi)Zn۳, (FeCoMnNiCr)۳Sn۲, (FeCoNiMn)۳Sn۲ and Cu۳(InSnSbGaGe) HEICs fabricated by induction melting are studied. The magnetic properties of the HEICs was determined mainly by the nature of the magnetic momentum of the constituent elements. (CoCuFeMnNi)Al and (CoCuFeMnNi)Zn۳ displayed ferromagnetic behavior at ۵ K, while indicated linear dependency of magnetization vs. magnetic (i.e. paramagnetic or antiferromagnetic state) at ۳۰۰ K. The magnetization of (FeCoMnNiCr)۳Sn۲, (FeCoNiMn)۳Sn۲ and Cu۳(InSnSbGaGe) HEICs at ۳۰۰ K exhibited a nearly linear dependency to magnetic field. Among all the investigated samples, (CoCuFeMnNi)Al exhibited the best magnetic properties with a saturation magnetization of about Ms = ۶.۵ emu/g and a coercivity of about Hc = ۱۰۰ Oe.

کلیدواژه ها:

High entropy intermetallic compounds ، Crystal structure ، Magnetic properties