The viscoelastic properties and the adhesion of pressure-sensitive adhesives (PSAs) are affected bythe test conditions in addition to the formulation. Herein, the adhesion properties of a poly(۲-ethylhexyl acrylate-acrylic acid) copolymer containing ۰.۲ and ۰.۳ wt. % crosslinking agent withrespect to the copolymer was evaluated in a probe tack test at debonding rates of ۵, ۵۰ and ۱۰۰mm/min. Increasing the test rate caused an increase in the maximum strain, maximum debondingstress and adhesion energy, as well as the occurrence of strain-hardening behaviour in both PSAs.Increasing the degree of crosslinking also caused a decrease in the maximum strain and adhesionenergy and an increase in the maximum stress, up to a rate of ۵۰ mm/min.

کلیدواژه ها:

Adhesive ، Acrylic Copolymer ، Probe Tack Test ، Debonding Rate ، Viscoelasticity.