Synthesis of coated iron oxide nanoparticles and feasibility study of their use in magnetic hyperthermia
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 112
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_PPAM-3-1_009
تاریخ نمایه سازی: 26 شهریور 1403
چکیده مقاله:
The unique properties of magnetic nanoparticles have made them useful and important particles for use in various fields, especially in heat-based applications. This research presents a hopeful facet of magnetic hyperthermia by superparamagnetic Fe۳O۴/Alumina nanoparticles. We synthesized Fe۳O۴/Alumina nanoparticles of different sizes by sonochemical method and evaluated their ability to generate heat. We found by characterizations with Field emission scanning electron microscopy (FE-SEM), X-ray diffraction technique (XRD), and Transmission electron microscopy (TEM) the samples to be of spherical shapes and spinel structure whose diameter could be controlled in the range from ۱۵ to ۲۵ nm. The magnetic behavior of the samples determined using a vibration sample magnetometer (VSM) showed hysteresis loops with a coercivity (HC) close to zero, suggesting superparamagnetic behavior at room temperature. The saturation magnetization (MS) for sample ۳ after synthesis is ۲۳ emu/g. We also investigated the potential of the samples for magnetic hyperthermia using alternating magnetic fields at various frequencies. Samples ۱, ۲, and ۳ achieved heat production rates of ۰.۲۲ °C/min, ۰.۴۱ °C/min, and ۰.۶۲ °C/min respectively under an alternating magnetic field with an amplitude of ۱۲۰ Oe and a frequency of ۲۵۰ kHz.
کلیدواژه ها:
نویسندگان
Saleh Fallah Samakosh
Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
Ali Bahari
Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
Vaheed Fallah Hamidabadi
Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
Hossain Milani Moghaddam
Department of Solid State Physics, University of Mazandaran, Babolsar, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :