Fabrication of a Polyetherimide/ZIF-۸ Composite Membrane for Separating Carbon Dioxide from Methane
محل انتشار: مجله تکنولوژی گاز، دوره: 8، شماره: 1
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 81
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JGT-8-1_005
تاریخ نمایه سازی: 18 مرداد 1403
چکیده مقاله:
In the present work, a polyetherimide/ZIF-۸ composite membrane was fabricated by solution casting technique. The prepared membranes were Characterized using Scanning Electron Microscopy (SEM), Fourier transform infrared spectroscopy – attenuated total reflectance (FTIR-ATR), energy dispersive X-ray (EDAX) and X-ray diffraction (XRD). Furthermore, the membrane's performance in separating carbon dioxide and methane was analyzed through single gas permeability measurements. FTIR-ATR spectrum of the prepared membrane confirmed the functional groups of polyetherimide. XRD analysis showed that the additive was well dispersed in the polymer, resulted in a reduction in the membrane's crystallinity. EDAX analysis confirmed the existence and proper dispersion of Zn particles in the membrane. Finally. The results of permeability tests showed that adding ZIF-۸ to the membrane significantly increased its permeability and selectivity. The permeability of the composite membrane for CO۲ gas was ۵.۹۱ GPU, more than twice that of the pure polyetherimide membrane. Additionally, the permeability for CH۴ gas was ۰.۳۱ GPU, representing a significant improvement over the pure membrane's permeability of ۰.۱۷ GPU. The carbon dioxide/methane selectivity also rose from ۱۵.۳ in the pure membrane to ۱۹.۱ in the composite membrane. In conclusion, the study demonstrated that adding ZIF-۸ to a polyetherimide matrix can improve the effectiveness of the resulting composite membrane for separating CO۲ from CH۴. The improvement in selectivity was primarily due to the increased solubility coefficient of carbon dioxide compared to methane in the composite membrane.
کلیدواژه ها:
نویسندگان
Omid Alizadeh
Assistant professor, Department of Chemistry and Chemical Engineering, Rasht Branch, Islamic Azad University, Rasht, Iran
Shiva Falahati
Graduate student, Department of Chemistry and Chemical Engineering, Rasht branch, Islamic Azad University, Rasht, Iran
Masoud Mokhtary
Professor, Department of Chemistry and Chemical Engineering, Rasht Branch, Islamic Azad University, Rasht, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :