Effect of Heat Treatment and Rolling on the Microstructure and Tensile Behavior of Twin-Roll Cast AA۸۰۰۶ Aluminum Foils

The Microstructure and tensile properties of ۶۰ µm thick AA۸۰۰۶ aluminum foil were investigated in the present study. Sheets of AA۸۰۰۶ were produced by twin-roll casting (TRC) with a thickness of ۸ mm and were reduced to ۴.۵ mm thickness by one pass of rolling. The sheets were heat-treated, homogenized and annealed. After heat treatment, both processes were subjected to cold rolling to compare their tensile properties in ۶۰ µm thickness after final annealing at different temperatures. The results showed that after homogenization, the short rod like eutectic phase is dispersed homogeneously in Al matrix of homogenized TRC processed alloy. The EDS results show that the contents of iron and manganese elements in the eutectic phase of TRC processed alloys decrease after homogenization, with the difference that this decrease is more noticeable in the thickness of ۴.۵ mm after annealing. It was also found that the homogenized sheet with a thickness of ۶۰ micrometers after a rolling step was compared to the homogenized sheet after casting, due to smaller spherical intermetallic particles and better grain structure after heat treatment, the relative elongation from ۱۲% to ۲۷.۵% showed an increase.

کلیدواژه ها:

aluminum ، Rolling ، Microstructure ، Mechanical properties