Chemical State Analysis of Magnesium-Supported Ziegler-Natta Catalyst by Soft X-ray Emission Spectrometer (SXES) after Contact with Alkyl Aluminum
محل انتشار: فصلنامه پلی اولفین ها، دوره: 11، شماره: 2
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 186
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-11-2_005
تاریخ نمایه سازی: 23 خرداد 1403
چکیده مقاله:
This report is on the characterization of active Ti center in heterogeneous Ziegler-Natta catalysts with Soft X-ray Emission Spectrometer (SXES). Since titanium in the catalyst has various chemical bonds, it is important to grasp the chemical bond state. The outermost shell electrons are very important for understanding the chemical bond state. SXES is the only method that can easily observe outermost shell electrons with current analytical instruments. Here, a co-milled solid of MgCl۲, TiCl۴, and Phthalate was used as a catalyst precursor, and three types of catalysts with significantly different catalytic activity levels were synthesized by changing the subsequent preparation process. The correlation between catalytic activity and the signal shape of Lα,β emission, which is the outermost shell electron of Ti in SXES analysis, was investigated. Lα,β emission was detected as broad signal. It could be observed that the high active catalyst had relatively strong signal intensity at the high energy side. The shape changes were also checked when the catalyst solids were treated by triethylaluminium. By this treatment, the relative intensity of the high energy side signal was further enhanced, suggesting that triethylaluminium treatment induced the elimination of inactive Ti from the catalyst solid. By comparing with the solid ۱۳C-NMR analyses data of the Ziegler-Natta catalyst described in our previous report, the high energy side signal of Ti Lα,β in SXES results implies the relationship with the NMR results for carbonyl function.
کلیدواژه ها:
Ziegler-Natta catalyst ، propene polymerization ، soft X-ray emission spectrometry (SXES) ، field emission scanning electron microscopy (FE-SEM) ، polymerization activity ، outermost shell electrons of titanium
نویسندگان
Masayoshi Saito
Analysis Center, Toho Titanium Co., LTD., ۳-۳-۵, Chigasaki, Chigasaki-City, Kanagawa, ۲۵۳-۸۵۱۰, Japan
Hiroshi Kashimura
Analysis Center, Toho Titanium Co., LTD., ۳-۳-۵, Chigasaki, Chigasaki-City, Kanagawa, ۲۵۳-۸۵۱۰, Japan
Takuo Kataoka
Analysis Center, Toho Titanium Co., LTD., ۳-۳-۵, Chigasaki, Chigasaki-City, Kanagawa, ۲۵۳-۸۵۱۰, Japan
Masahide Murata
Former Toho Titanium Co., LTD, Japan
Yusuke Sakuda
JEOL Ltd., ۳-۱-۲ Musashino, Akishima, Tokyo ۱۹۶-۸۵۵۸, Japan
Hiroyuki Yamada
JEOL Ltd., ۳-۱-۲ Musashino, Akishima, Tokyo ۱۹۶-۸۵۵۸, Japan
Hideyuki Takahashi
JEOL Ltd., ۳-۱-۲ Musashino, Akishima, Tokyo ۱۹۶-۸۵۵۸, Japan
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :