Study on Tablet conversion by pressure-less sintering method on the thermoluminescent dosimetric response of Beta Tricalcium Phosphate
محل انتشار: فصلنامه فیزیک و مهندسی پرتو، دوره: 5، شماره: 2
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 80
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_RPE-5-2_001
تاریخ نمایه سازی: 30 فروردین 1403
چکیده مقاله:
In this research work, commercial beta-tricalcium phosphate powder is converted into tablets by pressure-less sintering method. Thermoluminescence responses of tablet and powder samples in the dose range of ۲۰ to ۱۵۰۰ Gy have been compared and effective factors in tablet conversion such as mass in the range of ۳۰ to ۶۰ mg, force between ۱ to ۳ N, concentration of granulating solution and tablet diameter in the range of ۰.۴ to ۱۵ mm are investigated based on the results of dosimetric response and tablet hardness. The results show that by turning into tablets, the grain size increases, and the possibility of the first-order kinetics increases by the conversion of powders into tablets. It is possible to achieve a better dosimetric response than the it’s powder by applying suitable conditions for turning into tablets; also, the diameter of the sample can affect hardness, and it is better to make the tablets with a smaller size. Based on the results obtained from fading, reproducibility, sensitivity, peak shaping of the glow curve, and microhardness measurement, it can be seen that the samples that have been subjected to less pressure perform better and in order to achieve the desired results of converting to TLD dosimetry tablets, it is better to use more mass for tablets if more pressure is needed.
کلیدواژه ها:
نویسندگان
Hora Kavarian
Department of Physics, K.N. Toosi University of Technology, Tehran, Iran
Armin Mosayebi
Radiation Application Research School, Nuclear Science and Technology Research Institute, Tehran, Iran
Hamideh Daneshvar
Radiation Application Research School, Nuclear Science and Technology Research Institute, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :