Solving the cracking issue of grade ۷۲۲۵D sizes ۴۰ to ۶۵millimeters
سال انتشار: 1402
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 77
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
MCONF07_118
تاریخ نمایه سازی: 19 فروردین 1403
چکیده مقاله:
There is an agreement that the ۷۲۲۵D steel is amongst the most applicable steel grades in theworld, as when it is lower in diameter, the cooling rate is sufficiently high. Steel with a diameterless than ۴۰ mm is usually quenched in an oil medium while sizes bigger than ۶۵ mm are oftenwater-quenched. However, the main concern is the diameter sizes between ۴۰ to ۶۵ mm. Thisis the critical diameter range which means if water quenched, they are prone to cracking and ifoil cooled, their tensile strength is below average. The proposed solution to this issue was twostepquenching so that firstly the material was water-quenched up to the nose in its TTTdiagram and then oil-quenched. Another way is limiting the composition range and dopingaluminum with a smaller grain size and typically higher impact energy to the alloy. Finally,the application of polymers rather than water has completely overcome this issue.
کلیدواژه ها:
نویسندگان
Mohammad Hossein Amini Rad
Sales Engineer at IASCO., IASCO, Yazd, Iran
Reza Rezaei
Former head of the heat treatment section at IASCO., IASCO., Yazd, Iran