Structure development of Al-Zn-Cu/Al3Mg2 composite fabricated by mechanical alloying
محل انتشار: دومین کنفرانس بین المللی آلومینیوم
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,938
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC02_039
تاریخ نمایه سازی: 12 اردیبهشت 1392
چکیده مقاله:
In the current study, the effect of milling time on the grain size of Al-Zn-Cu/Al3Mg2 composite was investigated. In order to produce the composite, Al3Mg2 milled powders as a reinforcement particles were added to Al-Zn-Cu milled powder as a matrix phase and then they were milled together. Different milling times (10, 15 and 20 hours) were used in this study. XRD analysis and Scanning Electron Microscopy (SEM) were used to investigate the grain size of the milled composite powder. The result indicates that the optimum milling time to achieve the lowest grain size is 20 hours. Longer milling times (more than 20 hours) were found to be unsuitable due to the declined Al3Mg2 grain size resulted from the expansion of Al3Mg2 particle special surfaces. Therefore, this phenomenon causes more reaction between the particles and environment which results in burning lost of the particles.
کلیدواژه ها:
نویسندگان
M. Mirhendi
School of metallurgy and materials engineering, University of Tehran, Tehran, Iran
M. Emamy
School of metallurgy and materials engineering, University of Tehran, Tehran, Iran
H. Ramezanalizadeh
School of metallurgy and materials engineering, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :