چکیده مقاله:
Ultra-high molecular weight polyolefin (UHMWPO) has enormous potential applications due to their excellent mechanical properties such as tensile strength, flexural modulus, toughness and outstanding chemical resistance. But the processing of polyolefin, in particular, UHMWPO fibers cannot be processed by conventional methods due to its very high melt viscosity. In this work, we synthesized isotactic ultra-high molecular weight polypropylene (UHMWPP) resin and studied the processability of UHMWPP fibers using gel spinning and investigated physicomechanical properties. UHMWPP gel was made at various concentrations in decalin solvent at ۱۵۰°C to produce consistent spinning dope solutions. The ۷ wt.% concentration of UHMWPP was deemed best for fiber creation, compared to ۳ wt.% and ۵ wt.%. A rheological time sweep was done to ensure the gel's stability at ۱۷۰°C before the spinning process. The UHMWPP's gelation and fiber formation were studied by tweaking the gel concentration and adjusting the processing temperature. The resulting UHMWPP monofilament had a measure of ۲۲۰-۲۵۰ denier. The hot stretched fibers were analyzed with the scanning electron microscope (SEM) to understand the surface morphology of the fibers. The crystal morphology of UHMWPP fibers was measured with wide-angle x-ray scattering (WAXS) and DSC. The X-ray measurement of hot stretched UHMWPP fibers showed crystalline peaks compared to those without stretched fibers.
کلیدواژه ها:
نویسندگان
Parthiv Trivedi
Polymer Synthesis & Catalysis Division, Reliance Research & Development Centre, RCP, Reliance Industries Limited, Ghansoli-۴۰۰۷۰۱, Navi Mumbai, Maharashtra, India
Sandip Patil
E-Spin Nanotech Pvt. Ltd., IIT Kanpur, Uttar Pradesh, India
Virendra K. Gupta
Polymer Synthesis & Catalysis Division, Reliance Research & Development Centre, RCP, Reliance Industries Limited, Ghansoli-۴۰۰۷۰۱, Navi Mumbai, Maharashtra, India
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :