Characterization of Flowability and Compaction Behavior of Biomedical Ti-Cu Intermetallic Alloy Synthesized by Mechanical Alloying Method
محل انتشار: مجله سرامیک های پیشرفته، دوره: 9، شماره: 2
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 42
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-9-2_002
تاریخ نمایه سازی: 30 بهمن 1402
چکیده مقاله:
This study investigated the flowability and compactability of the milled Ti-Cu alloys as a new version of biomedical alloys used for fabrication via Additive Manufacturing. In this study, Ti- ۵۰ at. % Cu powder was first milled for different durations, and the morphology, microhardness, size, flowability, and compactability of the powder were assessed. The results indicated that while flowability increased with prolonged milling time, compressibility decreased owing to a decrease in the plastic deformation capacity. The highest flowability level was obtained when hard TiCu phase was synthesized after ۳۰ hours of milling. Different linear and nonlinear compaction equations were used to investigate the densification response of TiCu powder in a rigid mold during uniaxial compression. Cooper-Eaton nonlinear equation was found to be the best fit compared to the linear equation. The contribution of particle rearrangement to the densification behavior was high, and it increased upon increasing the applied pressure. At pressures below ۱۲۰۰ MPa, the contribution of plastic deformation to the powder densification was negligible.
کلیدواژه ها:
نویسندگان
Mohammad Reza Akbarpour
Professor, Department of Materials Engineering, Faculty of Engineering, University of Maragheh, Maragheh, P.O. Box ۸۳۱۱۱-۵۵۱۸۱, Iran
Solmaz Moniri Javadhesari
Assistant Professor, Department of Biology, Faculty of Basic Sciences, Azarbaijan Shahid Madani University, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :