Comparative Adsorption Study of Functionalized Magnetite and Maghemite Nanoparticles Coated with CTAB Surfactant for Efficient Chromium Removal from Wastewater
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 37
فایل این مقاله در 17 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JWENT-9-1_005
تاریخ نمایه سازی: 28 بهمن 1402
چکیده مقاله:
In this study, maghemite and magnetite nanoparticles were functionalized with cetyl trimethyl ammonium bromide(CTAB) surfactants, in order to obtain effective chromium removal from wastewater. X-ray diffractometry (XRD), transmission electron microscopy (TEM), and Fourier-transform infrared spectrophotometry (FTIR) were used to characterize the functionalized nanoparticles. Various parameters, including pH, initial chromium concentration, added salt, and adsorbent dose, were evaluated in batch experiments to evaluate chromium removal efficiency. Adsorbent dose and chromium ions show a synergistic relationship with pH and the chemical and electrostatic interactions between cationic surfactant and negatively charged Cr(VI) ions. In both types of functionalized nanoparticles, Cr(VI) was efficiently removed at low pH values with CTAB@MNPs, but the pH increased negatively impacted the removal process. Additionally, Fe۳O۴@CTAB mainly adsorbs chromium chemically, reducing Cr(VI) to Cr(III), with less impact from competitive ions compared with γ-Fe۲O۳@CTAB.At pH = ۲, adsorbent dose = ۵ g/L, and initial chromium concentration = ۱ mg/L, maghemite@CTAB achieved a high chromium removal efficiency of ۹۵%. In contrast, magnetite@CTAB achieved a chromium removal efficiency of ۹۵.۷۷% in ۷ minutes and ۳۰ seconds at pH = ۴, adsorbent dose = ۱۲ g/L, and initial chromium concentration = ۹۸ mg/L. Notably, magnetite outperformed maghemite by a factor of ۱۰۰ in chromium elimination, which can be attributed to the presence of two adsorption mechanisms, chemical and physisorption, in magnetite nanoparticles, whereas maghemite only had physisorption.
کلیدواژه ها:
Maghemite nanoparticles ، Magnetite nanoparticles ، Cetyl trimethyl ammonium bromide (CTAB) surfactants ، Chromium removal ، Adsorption efficiency
نویسندگان
Mohamed Naous
Department of Sciences and Technology, Faculty of Applied Sciences, Ibn Khaldoun University of Tiaret, Tiare ۱۴۰۰۰, Algeria
Ahmed Halfadji
Department of Sciences and Technology, Faculty of Applied Sciences, Ibn Khaldoun University of Tiaret, Tiare ۱۴۰۰۰, Algeria
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :