In-situ synthesized phases during the spark plasma sintering of g-C۳N۴ added TiB۲ ceramics: A thermodynamic approach

In this study, in situ composite was manufactured by using TiB۲ matrix and C۳N۴ additive through spark plasma sintering. The optimum SPS parameters were considered and the process was carried out at a temperature of ۱۹۰۰°C for ۷ minutes by applying an external pressure of ۴۰ MPa. The thermodynamics of possible reactions during the process were investigated. The products of the chemical reactions were identified. The complementary XRD investigations, the EDAX analysis and SEM microscopy were used to confirm the in-situ formation of new phases. The results showed that the used carbon nitride was decomposed into its constituents, i.e. carbon and nitrogen, and the BN phase has been formed as a result of chemical reactions.In this study, in situ composite was manufactured by using TiB۲ matrix and C۳N۴ additive through spark plasma sintering. The optimum SPS parameters were considered and the process was carried out at a temperature of ۱۹۰۰°C for ۷ minutes by applying an external pressure of ۴۰ MPa. The thermodynamics of possible reactions during the process were investigated. The products of the chemical reactions were identified. The complementary XRD investigations, the EDAX analysis and SEM microscopy were used to confirm the in-situ formation of new phases. The results showed that the used carbon nitride was decomposed into its constituents, i.e. carbon and nitrogen, and the BN phase has been formed as a result of chemical reactions.

کلیدواژه ها:

UHTC ، Spark plasma sintering ، Graphitic carbon nitride ، Composite