Investigation and fabrication of porous alumina bodies with unidirectionalporosity by freeze casting method
محل انتشار: دهمین کنگره سرامیک ایران
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 82
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICC10_026
تاریخ نمایه سازی: 16 بهمن 1402
چکیده مقاله:
Alumina Porous materials due to their exclusive properties were used in various applicationssuch as filtration filtration and catalyst supports. In this study, porous bodies were fabricated by freezecasting and conversion slip concentration. As a result for achieving optimum porositypercentage, ۸۲% solid content was necessary. Samples were frozen unidirectionally due toformation of unidirectional porosity. XRD patterns of samples are shown that the dominatedphases are corundum. SEM micrographs of samples microstructures indicate unidirectionalmorphology of porosity in the bodies. The porosity widths are in order of ۵ microns.
کلیدواژه ها:
نویسندگان
Saviz Parsa Saeb
Master student of Materials Engineering, School of Metallurgy and MaterialsEngineering, Iran University of Science and Technology
Farhad Golestanifard
Professor of Materials Engineering, School of Metallurgy and Materials Engineering,Iran University of Science and Technology
Hamidreza Rezaie
Professor of Materials Engineering, School of Metallurgy and Materials Engineering,Iran University of Science and Technology