Evaluation of Several Austenitic Types of Stainless Steel's Chemical Corrosion Resistance

This study aims to evaluate the efficacy of compounds as corrosion inhibitors for stainless steel in hydrochloric acid solution using gravimetric technique and electrochemical measurements. Stainless steel is resistant to corrosion and rust due to its chromium content, which reacts with oxygen in the air to form a protective coating. Passivation is the process of creating a thin layer of chrome oxide when exposed to oxygen, preventing rust. In this investigation, corrosion inhibitors made from benzoic acid derivatives were applied to ۳۱۶ stainless steel in a ۰.۵ M hydrochloric acid solution. The outermost parts of the investigated stainless steel samples were examined using scanning electron microscopy and energy dispersive spectroscopy. The study also assessed the fundamental properties of the studied inhibitors using the dynamic molecular simulation method. The best inhibitor concentration for C۳ at ۲۹۱ K was ۱.۰ ۱۰۲ M, resulting in the highest inhibition efficiency (۸۸%).In light of the concentrations of the antagonists under research and the impact of ambient the temperature, the current research investigates the efficacy of inhibition. The best inhibitor concentration for C۳ at ۲۹۱ K was ۱.۰ ۱۰۲ M, and this resulted in the highest inhibition efficiency (۸۸%).

کلیدواژه ها:

Stainless steel ، types ، chemical corrosion ، Resistance