A practical criterion for synthesizing ethylen-۱-butene copolymer in powder form in slurry polymerization with a Ziegler-Natta catalyst and predicting its incorporated ۱-butene
محل انتشار: فصلنامه پلی اولفین ها، دوره: 10، شماره: 4
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 69
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-10-4_006
تاریخ نمایه سازی: 5 آذر 1402
چکیده مقاله:
The concentration of ethylene and ۱-butene in n-hexane as polymerization media was calculated at five different pressure levels (۴, ۶, ۸, ۱۰, and ۱۲ bar) and four different ۱-butene concentrations (۰.۱۳, ۰.۲۶, ۰.۳۹, and ۰.۵۲ mol/L) in n-hexane at T= ۸۰°C using the Peng-Robinson thermodynamic equation of state. Some combinations of conditions were selected to perform the copolymerization reaction in the presence of an industrial TiCl۴/MgCl۲ Ziegler-Natta catalyst. The forms of the synthesized products were visually and qualitatively classified as either powder or sticky. The percentage of incorporated ۱-butene comonomer into the polyethylene chains was analyzed using calibrated FTIR tests. It was shown that for ethylene/۱-butene concentration ratios (β) in n-hexane above approximately ۱.۸۰, the product forms as a powder. For values below ۱.۳۰ threshold, the product was sticky. Thus, this ratio could be used as a criterion for selecting the proper combination of copolymerization pressure and ۱-butene concentration when aiming to achieve a powdered form of the product. It was shown that β has a strong correlation with the weight percentage of ۱-butene in the final LLDPE polymer. Therefore it can be used as an accurate prediction for wt.% of incorporated ۱-butene into the LLDPE chain within the studied concentration ranges with the specific catalyst system utilized.
کلیدواژه ها:
Zeigler-Natta catalyst ، LLDPE ، ethylene-۱-butene copolymerization ، ۱-butene incorporation ، Peng-Robinson Equation of State
نویسندگان
Mohsen Javaheri
Polymerization Engineering Department, Iran Polymer and Petrochemical Institute (IPPI), P.O. Box ۱۴۹۷۵/۱۱۲, Tehran, Iran
Mehdi Nekoomanesh
Polymerization Engineering Department, Iran Polymer and Petrochemical Institute (IPPI), P.O. Box ۱۴۹۷۵/۱۱۲, Tehran, Iran
Yousef Jahani
Department of Plastics, Faculty of Polymer Processing, Iran Polymer and Petrochemical Institute, PO Box ۱۴۹۶۵/۱۱۵, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :