Effect of SiC nanoparticles on dispersion of carbon nanotubes and grain refinement in Cu/MWCNTs composites
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,453
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_677
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
Small amount of SiC nanoparticles ( 2 vol.%) was added to the mixture of Cu/CNT as an active mixing agent for dispersing of the CNTs in Cu powder, and also as an agent to increase the matrix grains stabilityduring consolidation. The powders were mechanically ball milled for 3h in an optimized condition todisperse reinforcements in copper powder and to retain CNTs structure during processing. The composites with different volume fraction of CNTs were consolidated by hot pressing (HP) method.Microstructures of the powders and bulk materials were studied using scanning electron microscope(SEM), X-ray diffraction (XRD), Raman spectroscopy and High resolution transmission electron microscope (HR-TEM). The results showed relatively intact and uniform distribution of CNTs and fine matrix grain size due to addition of SiC nanoparticles. Raman characterization confirmed the retention ofCNTs structure in the composites during mechanical milling and HP. It can be concluded that dualreinforcement dispersion method can be used to strengthen the composite by improvement of the CNTs dispersion and grain refinement
کلیدواژه ها:
نویسندگان
M.R Akbarpour
Ceramic Department, Materials and Energy Research Center (MERC), P.O. Box ۱۴۱۵۵-۴۷۷۷, Tehran, Iran.
E Salahi
Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box ۱۱۳۶۵-۹۴۶۶, Tehran,
F Alikhani Hesari
Ceramic Department, Materials and Energy Research Center (MERC), P.O. Box ۱۴۱۵۵-۴۷۷۷, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :