CREEP BEHAVIOR OF ALUMINUM REINFORCED BY 1WT.% NANOSTRUCTURE ALUMINUM NITRIDE
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,401
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_221
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
In response to the demands for better mechanical properties and in an attempt to produce light weight materials considering the especial features of aluminum, researchers worldwide have beenexploring various techniques to strengthen aluminum in a cost-effective way. In this study 1wt. % AlN nanoparticles have been incorporated into aluminum matrix by milling air-atomized commercial pure aluminum with AlN nanoparticles in a planetary ball mill under an argon atmosphere for 12 hours. The powder has then been cold-pressed and hot extruded at an extrusion ratio of 27:6. The extruded rods were then machined to the creep samples and were creep-tested at variable constant loads from o.5 to o.65 KN at temperatures of 523K&573K.The test results reveal an improvement in the creep behavior of aluminum due to the incorporation of AlN nanoparticles.
کلیدواژه ها:
نویسندگان
Sedigheh Pirsalami
Master Student, Department of Materials Science and Engineering ,Shiraz University ,Iran.
Seied Ahmad Jenabali Jahromi
Professor, Department of Materials Science and Engineering, Shiraz University ,Iran.
BaBak Hashemi
Associate Professor, Department of Materials Science and Engineering ,Shiraz University ,Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :