SYNTHESIS AND CHARACTERIZATION OF NANO γ–ALUMINA BY SOLUTION COMBUSTION SYNTHESIS
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,091
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_148
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
Nanocrystalline γ-Al2O3 powders have been synthesized by a novel combustion method (SCS) using glycine as the fuel. The effectiveness and influence of pH and oxidizer/fuel ratio on the specific morphology and crystallite size of alumina particles was investigated respectively. With decreasing the pH values in the precursor solutions, the obtained materials could be modified from segregated nanoparticles (pH=10) to a flaky morphology (pH=2). Also, Results demonstrated that the alumina nanoparticles obtained from φ=1.6 had crystallite sizes around 45 nm which is less than other values of φ, due to evolution of larg amounts of gases which inhibits grain growth
کلیدواژه ها:
نویسندگان
N. Elahipanah
School of Metallurgy and Materials Engineering, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :