Wear behavior of carbon steel electrodeposited by nanocrystalline Ni–W coating
سال انتشار: 1388
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 75
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-6-2_003
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
Ni-W coatings, compared to pure nanocrystalline Ni, exhibit higher hardness and wear resistance. In some cases, these coatings are considered as environmental friendly alternatives for hard chromium coating. Till now, most of Ni-W coatings have been produced by direct current electrodeposition from alkaline baths. In this study square pulse current was used for deposition of Ni-W precipitates fromWattsbath. The effect of current density and duty cycle on morphology and wear behavior of nano-structured Ni-W coatings was investigated .The structure and morphology of the coatings were studied using X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques, respectively. Mechanical and tribological properties of the deposits were also investigated by means of microhardness and pin-on-disk wear tester. The results showed that a decrease in current density and duty cycle increased the W content of Ni-W coating. This increase led to an increase in hardness and improved the wear resistance of nanocrystalline coatings.
نویسندگان
A. Amadeh
School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, P.O.Box ۱۱۱۵۵-۴۵۶۳, Tehran, Iran
M. Harsij sani
School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, P.O.Box ۱۱۱۵۵-۴۵۶۳, Tehran, Iran
H. Moradi
School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, P.O.Box ۱۱۱۵۵-۴۵۶۳, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :