A Study of the Chemical Composition and Heat Treatment of Electroless Ni-B-Tl Alloy Coating on AISI ۳۱۶ Stainless Steel
سال انتشار: 1384
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 77
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-2-2_003
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
Despite having some useful properties, stainless steels suffer from lack of suitable surface hardness. In this research electroless Ni-B-Tl coating was used with the aim to increase their surface hardness. The effects of Nickel chloride, Sodium borohydride, Thallium nitrate and Ethylendiamin on the chemical composition of coating were studied. To achieve an increase in hardness, the effects of heat treatment on the hardness of the deposited layer at various temperatures, were also studied. The results showed that the deposition rate and surface hardness of the deposited layer were affected by the variation in concentration of bath components. The micro structure of the electroless Ni-B-Tl coating consists of nickel and super saturated solid solutions. It was also found that the hardness of the coating was increased due to the formation of Ni۲B and Ni۳B phases during heat treatment.
کلیدواژه ها:
نویسندگان
N. Parvini Ahmadi
Materials Engineering Faculty, Sahand University, Tabriz, Iran
R. Khosroshahi
Materials Engineering Faculty, Sahand University, Tabriz, Iran
M. Abdeli
Materials Engineering Faculty, Sahand University, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :