Recrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
سال انتشار: 1384
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 113
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-2-2_006
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has been applied to cold rolled samples and the resulted microstrucrures have been compared with the microstructure obtained from the box annealing process in MSP. It is found that at ۶۳۵ and ۷۰۰ºC the isothermal annealing produces equiaxed grains, while box annealing process presents an elongated grain structure. The recrystallization fractions have been measured using the point counting method. The linear intercept method has been employed to measure the grain size. It is revealed that at ۵۵۰ºC, in salt bath annealing, recrystallization is stopped after ۵۰% recrystallization with elongated new grains. Constant grain sizes upon holding after recrystallization at ۶۳۵ and ۷۰۰ºC during isothermal annealing show that the grain growth is stopped. Further holding at ۷۰۰ºC results an abnormal grain growth in the recrystalized microstructure. The hardness variations during annealing, with a decrease at the beginning of annealing followed by an increase trend at all temperatures, show a good consistency with microstructural observations. Investigation of the results leads to the conclusion that a precipitation process occurs during annealing which greatly affects both restoration processes and resulted microstructure as well as the properties. The effect of the precipitation process depends on the time of its occurrence with respect to each restoration process. A Relatively high value of ۳۱۵ KJ/mole for recrystallization activation energy has been related to the simultaneous occurrence of recrystallization and precipitation processes.
کلیدواژه ها:
نویسندگان
B. Soleimani Amiri
Department of Metallurgy, Shahid Bahonar University, Kerman, Iran
G. Akbari
International Center for Science and High Technology and Environmental Science, Kerman, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :