Evaluation of microstructure and mechanical properties of friction stir welded copper / ۳۱۶L stainless steel dissimilar metals
سال انتشار: 1389
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 81
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-7-2_005
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
In the present research, friction stir welding (FSW) process was used for butt joining of pure copper plate to ۳۱۶L stainless steel plate. Mechanical properties and microstructural characteristics of the joint were evaluated by microhardness and tensile tests as well as optical and scanning electron microscope (SEM). It was found that microstructure of the weld nugget (WN) has fine grains whereas the elongated grains are located in the thermo mechanically affected zone (TMAZ) into ۳۱۶L stainless steel. Also, coarse grains are observed in the heat affected zone (HAZ) into pure copper. The microhardness values of the WN are much higher than the base metals. The HAZ zone shows minimum hardness values. The butt joint has ۸۵% weld efficiency compared to the copper base meal.
کلیدواژه ها:
نویسندگان
A. Najafkhani
Department of Materials Engineering, MUT, Tehran ۱۵۸۷۵-۱۷۷۴, Iran
K. Zangeneh-Madar
Department of Materials Engineering, MUT, Tehran ۱۵۸۷۵-۱۷۷۴, Iran
H. Abbaszadeh
Department of Materials Engineering, MUT, Tehran ۱۵۸۷۵-۱۷۷۴, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :