Welding of ۳۰۴L Stainless Steel with Activated Tungsten Inert Gas Process (A-TIG)
سال انتشار: 1392
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 97
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-10-1_005
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
Gas tungsten arc welding is a popular process in those applications requiring a high degree of quality and accuracy. However, this process has a big disadvantage against the substantially high productivity welding procedures. Hence, many efforts have been made to improve its productivity. One of these efforts is the use of activating flux (A-TIG welding). In this study, the performance of A-TIG welding on ۳۰۴L austenitic stainless steel plates has been presented. Two oxide fluxes, TiO۲ and SiO۲ were used to investigate the effect of A-TIG welding process on weld morphology, microstructure and mechanical properties of weldments. The experimental results indicated that A-TIG welding could increase the weld penetration and depth-to-wide ratio. It was also found that A-TIG welding could increase the delta-ferrite content of weld metals and improve the mechanical properties. Moreover, a ۲D axial symmetric model was developed to simulate the flow behavior in the melting pool. These results were compared to those experiments carried out on a stainless steel (۳۰۴L) melted by a stationary heat source.
کلیدواژه ها:
نویسندگان
E. Ahmadi
Faculty of Material Engineering, Sahand University of Technology, Tabriz
A. Ebrahimi
Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran
R. Azari Khosroshahi
Faculty of Material Engineering, Sahand University of Technology, Tabriz
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :