Investigating the effect of different anisotropic surface roughening methods on ionic polymer metal composites behavior
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 79
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JCARME-13-1_010
تاریخ نمایه سازی: 2 آبان 1402
چکیده مقاله:
As the smart materials, ionic polymer-metal composites (IPMCs), have a layered structure consisting of a polymeric membrane based on perfluorinated alkene, which is sandwiched between two noble metal-based electrodes, such as gold and platinum, and they can be bent significantly under applying a low-range of voltage. IPMCs are used in many applications, such as robotics, biomechanics, and medical purposes. In order to improve the performance of IPMC, in this article, three different anisotropic surface roughening methods with new and optimized fabrication instructions are used, and samples are compared. The experiments are applied to measure three main factors of IPMCs: displacement, blocking force, and lifetime. The results obtained from plasma samples show that the maximum displacement is ۳۶.۲۳ mm, the blocking force is ۴.۰۸ etching, ۱۸ percent higher lifetime than micro sandblasting, and sandpaper under applying a voltage range between ۱-۷ V; as a result, the plasma etched IPMC sample has the most efficiency.
کلیدواژه ها:
نویسندگان
Amirmehdi Mosaddeghi
Department of Mechanics, Electrical Power and Computer, Science and Research Branch, Islamic Azad University, Tehran, Iran.
Hamid Soleimanimehr
Department of Mechanics, Electrical Power and Computer, Science and Research Branch, Islamic Azad University, Tehran, Iran.
Ali Alinia ziazi
Department of Mechanics, Electrical Power and Computer, Science and Research Branch, Islamic Azad University, Tehran, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :