Study of Antibacterial Activity and Dyeability Property of PET/Cotton Fabrics Coated Ag/SiO۲ Nanocomposites
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 79
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJTNBM-2-2_002
تاریخ نمایه سازی: 2 آبان 1402
چکیده مقاله:
In present study, two components of Ag/SiO۲ nanocomposite were prepared by the Sonochemical method and then the PET/cotton fabric treated with Ag/SiO۲ nanoparticles (Ag/SiO۲ NPs) by Pad-Dry method. The treated fabric dyed at the optimum condition with direct dyes. The influence of the Ag/SiO۲ nanocomposite on the performance of PET/cotton fabric was investigated by the use of X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscope (SEM), electron dispersive X-ray spectroscope (EDX) and reflectance spectrophotometer (RS). TEM images of Ag/SiO۲ showed the particles size were ۳۰-۷۰ nm. SEM results of Ag/SiO۲ nanocomposite powders show that nanoscale particles are well formed, also SEM micrograph of treated fabrics indicated that the nanoparticles were well dispersed on the surface of sample. EDX results showed the presence of nanoparticles increased on the surface of samples with increase concentration of colloid solution nanoparticles. The antibacterial properties were determined by reduction growth of a Gram-negative bacterium E. coli and a Gram-positive bacterium Staphylococcus aureus. Photo-catalytic activities of the coated PET/cotton fabric were evaluated through the degradation of methylene blue under UV irradiation.
کلیدواژه ها:
نویسندگان
Laleh Maleknia
Department of Biomedical Engineering, South Tehran Branch, Islamic Azad University, Tehran, Iran
Elaheh Ahmadi
Nanotechnology Research Center, South Tehran Branch, Islamic Azad University, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :