The Post-fire Behavior of Lightweight Structural Concrete is Improved by Nano-SiO۲ and Steel Fibers
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 36، شماره: 11
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 138
فایل این مقاله در 19 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-36-11_001
تاریخ نمایه سازی: 22 مهر 1402
چکیده مقاله:
The primary goal of the engineering design of building is to reduce the weight of the structure and its resistance to fires and earthquakes because fires are inevitable. Hence, the direction of this study was to use lightweight concrete because of its unique advantages in weight loss and fire resistance due to its thermal insulation property. It was also intended to enhance the strength and behavior of this concrete at high temperatures. For this purpose, four mixing designs samples without fibers and nano-SiO۲, samples with different proportions of nano-SiO۲, samples with different proportions of fibers, and samples with both fibers and nano- SiO۲ together were prepared. The results showed damage to samples free of nano-SiO۲ and fibers, changing their color, reducing their resistance and reducing their weight. But adding nano-SiO۲ fibers or using them together leads to improving the properties of concrete at all temperatures. Due to nano- SiO۲, its pozzolanic interactions improve the microstructure, and the fibers prevent cracks in concrete. This study also dealt with the effect of changing the size of the samples on the compressive strength, and the results showed an increase in the resistance of the samples with small sizes, and resulted factors for converting the resistance of non-standard samples into a standard.
کلیدواژه ها:
نویسندگان
F. Altalib
School of Civil Engineering, Babol Noshirvani University of Technology, Babol, Iran
H. R. Tavakoli
School of Civil Engineering, Babol Noshirvani University of Technology, Babol, Iran
S. K. Hashemi
School of Civil Engineering, Babol Noshirvani University of Technology, Babol, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :