Numerical Study of the Effect of Temperature Changes on the Failure Behavior of Sandwich Panels with Honeycomb Core
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 134
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JADSC-2-2_001
تاریخ نمایه سازی: 15 مهر 1402
چکیده مقاله:
In this paper, failure modes of sandwich panels are investigated numerically using finite element method. For this purpose, four sandwich beams of GFRP laminate skins and Nomex honeycomb core are considered. The models have been chosen so that they could cover all failure modes according to available experimental failure mode maps. Models are created and analyzed based on standard ۳-points bending test, using ASTM standard C۳۹۳-۶۲. In order to investigate the effect of loading and sandwich panel parameters on failure behavior, finite element analysis has been utilized. The results are verified by comparing experimental and theoretical results. The constructed failure mode map shows dependence of failure mode on the ratio of skin thickness to span length, and honeycomb relative density. To Then, effect of temperature on the failure modes of sandwich panels, has been investigated. Results show that failure modes haven’t depended on environment temperature and failure load decreases by increasing environmental temperature. The slope of reduction is a function of beam geometrical parameters. Depending on the parameters, the failure loads decrease between ۱۰% to ۴۰% by increasing environmental temperature.
کلیدواژه ها:
نویسندگان
Ismaeil Eynali
Department of Mechanical Engineering, Ahvaz branch, Islamic Azad University, Ahvaz,, Iran.
Seyed Alireza Seyed Roknizadeh
Department of Mechanical Engineering, Engineering Faculty, Shahid Chamran University of Ahvaz, Ahvaz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :