Parametric Study of Reinforcement of Keyhole-less Friction Stir Spot Welding using Al۲O۳ and TiO۲ Nanopowders
محل انتشار: مجله شکل دهی مواد، دوره: 10، شماره: 2
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 88
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-10-2_007
تاریخ نمایه سازی: 14 شهریور 1402
چکیده مقاله:
In the present paper, two-stage refilled friction stir spot welding is used to join mild steel sheets with a thickness of ۲ mm. Meanwhile, alumina and titanium oxide nanopowders are also introduced to the nugget to achieve superior mechanical properties. Two non-consumable tools are used with and without pins to weld and refill the keyhole, respectively. Before refilling, the keyhole is filled with nanopowders which are then distributed by the pinless refilling tool. Three parameters are investigated; the rotational speed of the welding tool and the rotational speed and dwell time of the refilling tool. The tensile test is used to evaluate the strength of the joints. The microhardness is measured in the welding zone to evaluate the powder distribution. The results suggest an increase in the joint strength by ۴۲% and ۱۸% with alumina and TiO۲ as reinforcement, respectively. With a ۳۱.۹۴% contribution, the refilling tool rotational speed is the most effective input parameter affecting the joint strength. Considering the microstructure analysis and the microhardness test, the material flow pattern is mainly downward which results in the accumulation of the reinforcing powder in the lower sheet especially when a lower refilling tool rotational speed is used.
کلیدواژه ها:
نویسندگان
M. Salehi
Mechanical Engineering Department, University of Birjand, Birjand ۹۷۱۷۵-۳۷۶, Iran
S.M.H. Seyedkashi
Mechanical Engineering Department, University of Birjand, Birjand ۹۷۱۷۵-۳۷۶, Iran
M. Sajed
Mechanical Engineering Department, Azarbaijan Shahid Madani University, Tabriz, Iran
H. Rastegari
Department of Mechanical and Materials Engineering, Birjand University of Technology, Birjand, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :