Review of Damage Tolerant Analysis of Laminated Composites
محل انتشار: فصلنامه مکانیک جامد، دوره: 2، شماره: 3
سال انتشار: 1389
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 87
فایل این مقاله در 15 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JSMA-2-3_007
تاریخ نمایه سازی: 28 مرداد 1402
چکیده مقاله:
With advanced composites increasing replacing traditional metallic materials, the material inhomogeneity and inherent anisotropy of such materials lead to not only new attributes for aerospace structures, but also introduce new technology to damage tolerant design and analysis. The deleterious effects of changes in material properties and initiation and growth of structural damage must be addressed. The anisotropic and brittle properties make this requirement a challenging to composite structural designers. Accurate, reliable and user-friendly computational methods, design and analysis methods are vital for more damage tolerant composite structures. Both durability and damage tolerant methodologies must address the possible changes in mechanical properties and the evolving damage accumulations that may occur during the vehicle’s service lifetime. Delamination is a major failure mode in laminated composites and has received much research attention. It may arise out of manufacturing defects, free edge effects, structural discontinuities, low and high velocity impact damage, and even bird strikes. Early pioneering work established that the reduction in strength following delamination damages placed severe limits on the design allowable for highly loaded components such as aircraft wing and fuselage structure. In the present article, we provide a state-of-art survey on damage tolerant design correlated failure behavior and analysis methodologies of laminated composites. Particular emphasis is placed on some advanced formulations and numerical approaches for efficient computational modeling and damage tolerant analysis of laminated composites.
کلیدواژه ها:
Damage tolerant analysis ، Delamination ، Virtual crack closure-integral technique ، Cohesive zone model ، Progressive failure analysis
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :