The effects of anodizing condition and post treatment on the growth of nickel nanowires using Anodic Aluminum Oxide
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 7، شماره: 3
سال انتشار: 1389
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 59
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-7-3_005
تاریخ نمایه سازی: 26 مرداد 1402
چکیده مقاله:
The effects of anodizing condition and post treatment on the growth of nickel nanowires, were investigated. A two-step anodizing process was applied in phosphoric and oxalic acid solution. Nickel electrochemical plating was applied to fill Anodic Aluminum Oxide (AAO) pores. For pore filling enhancement, AAO surfaces were treated by silver predeposition. After electroplating, aluminum and oxide layer of some specimens were removed. The results showed that silver preplating increases the pore filling and as the applied voltage becomes higher, the pores diameter decreases.
کلیدواژه ها:
نویسندگان
Mohammadtaher Safarzadeh
Chalmers University of Technology
seyed Mohammad ali Boutorabi
Iran University of Science and Technology
Asghar Arab
Advanced Material Research Center, Iran University of Science and Technology,