EFFECT OF ANNEALING ON MICROSTRUCTURE AND CORROSION PERFORMANCE OF ADB AND ALB ALLOYS

Microstructure and corrosion performance of admiralty brass (ADB) and aluminum brass (ALB) alloys after passing different annealing heat treatments were investigated using optical and scanning electron microscope, energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), DC polarization measurements and electrochemical impedance spectroscopy (EIS). The results showed that heat treating of ALB caused gradient in aluminum concentration across the grains whose increased with increasing of annealing temperature. On the other hand, corrosion current density (i corr) of ADB in ۳.۵%NaCl media decreased with increasing of recrystallization, while ALB showed corrosion behavior inconsistent with ADB. The impedance measurements showed that corrosion rate of ADB decreased with increasing of exposure time from ۰ to ۱۵ days which could be related to the formation of SnO ۲ surface film and the Sn-rich phases. While polarization resistance of ALB decreased by passing days in the corrosive media which could be associated to establishing of differential aluminum concentration cells.

کلیدواژه ها:

Admiralty brass ، Aluminum brass ، Annealing ، Microstructure ، Corrosion resistance