EFFECT OF SPIRAL DESIGN ON CRYSTAL ORIENTATION DURING SINGLE CRYSTAL GROWTH
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 11، شماره: 2
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 39
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-11-2_005
تاریخ نمایه سازی: 26 مرداد 1402
چکیده مقاله:
Geometrical design of the spiral crystal selector can affect crystal orientation in the final single crystal
structure. To achieve a better understanding of conditions associated with the onset of crystal orientation in a spiral
crystal selector, temperature field was investigated using three-dimensional finite element method during the process.
Different geometries of spiral crystal selector were used to produce Al- ۳ wt. % Cu alloy single crystal using a
Bridgman type furnace. The Crystal orientation of the samples was determined using electron backscattered
diffraction (EBSD) and optical microscopy. Analysing the temperature field in the crystal selector revealed that, the
orientation of growing dendrites against liquidus isotherm in the spiral selector was the reason for crystal
misorientation which differs in various selector geometries. Increasing the take-off angle from ۳۵° up to ۴۵° increases
the misorientation with respect to direction. Further increase of take-off angle greater than ۴۵° will decrease
the crystal misorientation again and the efficiency of the selector to produce a single grain is decreased.
کلیدواژه ها:
نویسندگان
M. Ghanbari
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Iran, Tehran
M. R. Aboutalebi
Center of Excellence for High Strength Alloys Technology, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Iran, Tehran.
S. G. Shabestari
Center of Excellence for High Strength Alloys Technology, School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Iran, Tehran.