CHARACTERIZATION OF CO-FE MAGNETIC FILMS FABRICATED BY GALVANO-STATIC ELECTRODEPOSITION
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 14، شماره: 2
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 67
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-14-2_007
تاریخ نمایه سازی: 26 مرداد 1402
چکیده مقاله:
In this research, nanocrystalline Co-Fe coatings were electrodeposited on copper substrate. The influence of current density on different properties of the films at two pH levels was investigated. All the coatings showed nodular structure with rougher morphology at higher current densities. Due to anomalous deposition at higher current density, the amount of iron content increased and reached its maximum value at about ۵۰ wt.% for the coating obtained from pH ۵. X-ray diffraction patterns showed hcp structure as the dominant phase. However, by increasing current density at lower pH value, a double phase structure containing fcc+hcp phases was detected. It was observed that current density has a positive effect on grain refinement. However, coarser grains would obtain at lower pH value. Microhardness measurements showed that, there is a direct relationship between grain size and microhardness. Moreover, microstructure in double phase structure films can influence microhardness more dominantly. Vibrating sample magnetometer (VSM) measurements indicated that the saturation magnetic is proportion to deposited iron content and reached its maximum value at about ۱۵۱۲ emu/cm۳. It was cleared that grain size, phase structure and chemical composition can affect coercivity of the films effectively.
کلیدواژه ها:
نویسندگان
Z. Ghaferi
Department of Material Science and Engineering, Shahid Bahonar University of Kerman
S. Sharafi
Department of Material Science and Engineering, Shahid Bahonar University of Kerman
M.E. Bahrololoom
Department of Material Science and Engineering, Shiraz University
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :