STRUCTURAL AND IONIC CONDUCTIVITYSTUDIES ONPLASTICIZED PAN-SODIUM FLUORIDE POLYMER ELECTROLYTES FOR ELECTROCHEMICAL CELL APPLICATIONS
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 14، شماره: 4
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 60
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-14-4_001
تاریخ نمایه سازی: 24 مرداد 1402
چکیده مقاله:
Ion conducting gel polymer electrolytes based on poly acrylonitrle (PAN) complexed with different weight percent ratios of Sodium Fluoride (NaF) salt were prepared by using solution cast technique. Structural characterization was performed using X-ray diffraction (XRD) technique and Fourier transforms infrared (FTIR) spectroscope technique. From the X-rd results increase in amorphous phase with the increase of dopant salt concentration was observed. Fourier transform infrared (FTIR) spectroscopic analysis confirmed the complexation of the salt with the polymer matrix. Electrical conductivity was measured that the magnitude of ionic conductivity increased with the increase in the salt concentration as well as temperature. The surface morphology was observed by using Scanning Electron Microscope (SEM), the optical band gap measured from UV-Vis Spectroscopy. The sample containing ۳۰ wt% of NaF exhibited the highest conductivity of ۱.۸۲x۱۰-۴ S cm-۱ at ۳۰۳K and ۲.۹۶x۱۰-۳ S cm-۱ at ۳۷۳K. The temperature dependence of ionic conductivity of these films followed Arrhenius relation. Transference number measurements were carried out to investigate the nature of the charge transport species in the polymer electrolyte systems. The transference number data showed that the charge transports in these systems are predominantly due to ions. Using these polymer electrolyte films, electrochemical cells were fabricated and their discharge characteristics were studied. Various cell parameters, such as open circuit voltage, short circuit current, power density and energy density were determined.
کلیدواژه ها:
نویسندگان
N. Maragani
K.L.university
K. Vijaykumar
Dept. of Physics, Dayananda Sagar Academy of Technology and Management, Bangalore
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :