Milliliter-scale microbial fuel cell (MFC) fabricated by polyethersulfone (PES) hollow fiber membrane
محل انتشار: مجله طراحی فرآیندهای شیمیایی، دوره: 1، شماره: 2
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 125
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CPD-1-2_002
تاریخ نمایه سازی: 15 مرداد 1402
چکیده مقاله:
Microbial fuel cell (MFC) is a technology of increasing interest recently. However, the lack of efficient and cost-effective membranes has hampered the commercialization of MFCs. polyether sulfone (PES) hollow fiber was utilized as the separator in the cylindrical ml-scale active–air MFC to treat domestic wastewater. The conventional aeration unit replaced with the silicon membrane tube that was only passed the oxygen of air across wall membranes and provides appropriate dissolved oxygen in the cathode chamber. The increase in hydraulic retention time (HRT) (from ۱.۴۳ to ۳.۹۷ min) drastically improved the power and current densities of the MFC from ۳۰۶.۴۱±۱۷.۴۳ to ۵۴۰.۹۸ ±۳۲.۰۰ mW/m۲, and from ۱۸۴۲.۱۳۸±۱۰۳.۱۸ to ۲۱۹۱.۸۳±۱۶۰.۰۶ mA/m۲, respectively. The electricity generation performance gradually continued to grow by further extending the HRT from ۳.۹۷ to ۱۰.۱۹ min. The maximum power and current densities of ۵۸۲.۹۷±۲۸.۶۱ mW/m۲ and ۲۴۰۴.۱۵±۱۴۰.۶۱ mA/m۲ are obtained at the HRT of ۱۰.۱۹ min. Similarly, the coulombic efficiency as well as the current and voltage generation of the MFC is enhanced by the increment of HRT. The maximum open circuit voltage and current of ۷۶۸±۱۴.۱۰ mV, and ۰.۴۱۸±۰.۰۰۴ mA (with the external resistance of ۹۸۶ Ω) are yielded at the HRT of ۱۰.۱۹ min. The rather low response time which was obtained for this hollow fiber-MFC (۴۵۰ min) shows its potential applicability as a biosensor.
کلیدواژه ها:
Microbial fuel cell (MFC) ، Ultrafiltration Hollow fiber ، Domestic wastewater treatment ، Hydraulic retention time (HRT) ، Scale-down ، biosensor
نویسندگان
Vajihe Yousefi
. Chemical Engineering Department, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Davod Mohebbi-Kalhori
Chemical Engineering Department, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Abdolkarim Heydari
Chemical Engineering Department, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran