Evaluation of Corrosion Behavior of ۳۱۶ L Stainless Steel Manufactured by SLM Method After Heat Treatment and Surface Treatments

In recent years, selective laser melting (SLM) has attracted the attention of engineering active in this field due to its controllability, the possibility of producing parts with complex shapes and good surface properties. It has been found that by performing the next operation that takes place after the production of parts by SLM method, its surface properties such as corrosion and tribological properties can be improved. In this research, two types of subsequent treatments including heat treatment and surface mechanical treatment (shot peening) were investigated on the microstructure and corrosion behavior of the ۳۱۶L sample produced by SLM method. Examining the microstructure of the samples with the help of optical microscope images showed that surface treatment and heat treatment make the grains rougher and finer, respectively. The XRD pattern of the samples indicated the austenitic nature of the alloy produced by SLM method, which did not show any phase change on it by mechanical operation. While heat treatment caused the formation of oxide compounds such as chromium oxide. The corrosion behavior of the samples was evaluated using the cyclic polarization test. The results of this test showed the positive effect of the oxide layer formed during heat treatment on the corrosion behavior of the SLM sample. Also, the sample with both surface treatments showed the highest corrosion resistance due to having the lowest roughness and the presence of chromium oxide.

کلیدواژه ها:

Corrosion ، Phasing ، Heat treatment ، Selective laser melting