The effect of nanoclay on the creation of clusters of polyamide ۶ microfibrils
محل انتشار: فصلنامه علوم و فناوری ذرات، دوره: 8، شماره: 1
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 186
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JPST-8-1_004
تاریخ نمایه سازی: 28 فروردین 1402
چکیده مقاله:
The PA۶/clay nanocomposites were prepared during in-situ anionic ring-opening polymerization (AROP) via reactive melt blending in a Hakke internal mixer. Then, the samples were characterized using FT-IR, DSC, DMTA, rheometer, XRD, SEM/EDX/elemental mapping, TEM, and HT-GPC to study the effects of Cloisite ۱۵A on PA۶ properties. The results showed that nanoclay caused a decrease in the ultimate tensile strength (UTS), crystallinity, Tm, Tg, and tan δ of the samples. However, it increased the Young′s modulus and stress rupture of the samples. Furthermore, the nanocomposites showed a pseudo-solid behavior because of the reinforcing effect of the nanoparticles. Additionally, α crystals were not seen in the samples with ۱ and ۳ % nanoclay; however, γ crystals were observable in those samples. Also, nanoclay decreased PA۶ viscosity and increased dispersity and residual monomers in the nanocomposite samples. The nanoclays exfoliated in the sample have ۰.۵ % nanoparticles, but they were intercalated by more loading in the PA۶ matrix. Moreover, the PA۶ microfibrils were observed as sporadic and clay-centered clusters in the SEM micrographs of the pure and nanocomposite samples, respectively. Therefore, the clustering of PA۶ microfibrils in the matrix during in-situ AROP is considered a novelty in current research.
کلیدواژه ها:
نویسندگان
Roya Mashayekhi
Polymer and Textile Department, Islamic Azad University, South Tehran Branch, Tehran, Iran
Morteza Ehsani
Polymer and Textile Department, Islamic Azad University, South Tehran Branch, Tehran, Iran
Shervin Ahmadi
Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran
Ramin Khajavi
Polymer and Textile Department, Islamic Azad University, South Tehran Branch, Tehran, Iran
Hossein Ali Khonakdar
Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :