Microstructural Investigation into Premature Failure of Compressor Turbine (CT) Blade Material of High Pressure (HP) PT۶A-۱۱۴A Engine

سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 139

فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

JR_IJMSEI-16-1_006

تاریخ نمایه سازی: 1 اسفند 1401

چکیده مقاله:

This paper investigates premature failure of High Pressure (HP) PT۶A-۱۱۴A Compressor Turbine (CT) blades used for short-haul aircraft fleet at ۶۳۷۸ hours, contrary to ۱۰۰۰۰ hours pre-set by the manufacturer. The CT blades were sectioned both transversely and longitudinally and subjected to several microstructural examinations; X-ray Diffraction (XRD), X-ray Fluorescence (XRF), Energy Dispersive Spectroscopy-Scanning Electron Microscopy (EDS-SEM) of the tips, airfoils, as well as the bases. It was observed that from repeated elevated heating, incomplete solutioning and recrystallization of the substrate material, brittle carbides were initiated and developed. The tips were more affected, followed by the airfoils and least at the bases. Impingement of heat from the combustors on the CT blades led to rapid graining and rafting with eventual cracking upon cooling. The results further suggested that pores which are typically manufacturing defects were pronounced at the bases than either at the airfoils and the tips. However, contrary to the expectation that the bases would degrade more and rapider, a more near uniform distribution of the cuboidal phase was evident relative to the tips and airfoils, confirming that degradation of the CT blades originated from creep and fatigue.

کلیدواژه ها:

نویسندگان

J. Ngoret

Department of Mechanical Engineering, University of Botswana.

V. Kommula

Department of Mechanical Engineering, University of Botswana.

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Tamarin, Y., Protective coatings for turbine blades: ASM international, ۲۰۰۲ ...
  • Huang, Z., Wang, Z., Zhu, S., Yuan, F., and Wang, ...
  • Pollock and Tin, S., "Nickel-based superalloys for advanced turbine engines: ...
  • Swaminathan, V., Cheruvu, N., Klein, J., and Robinson, W., "Microstructure ...
  • Carter, T.J., "Common failures in gas turbine blades," Engineering Failure ...
  • Pineau, A. and Antolovich, S.D., "High temperature fatigue of nickel-base ...
  • Kianicová, M., "Microstructural Behaviour of Protective AlSi Coatings under Thermal ...
  • Becker, W.T., Shipley, R.J., Lampman, S.R., Sanders, B.R., Anton, G.J., ...
  • Kargarnejad, S. and Djavanroodi, F., "Failure assessment of Nimonic ۸۰A ...
  • Pahlavanyali, S., Wood, M., and Marchant, G., "Microstructural evolutions of ...
  • Zielińska, M., Sieniawski, J., Yavorska, M., and Motyka, M., "Influence ...
  • Jena, A. and Chaturvedi, M., "The role of alloying elements ...
  • Balikci, E. and Raman, A., "Characteristics of the γ′ precipitates ...
  • Zhao, K., Lou, L., Ma, Y., and Hu, Z., "Effect ...
  • Smith, G. and Patel, S., "The role of niobium in ...
  • Wallwork, G. and Hed, A., "Some limiting factors in the ...
  • Qin, X., Guo, J.T., Yuan, C., Hou, J.S., and Ye, ...
  • Liu, L., Jin, T., Zhao, N., Sun, X., Guan, H., ...
  • Pollock, T. and Field, R., "Dislocations and high-temperature plastic deformation ...
  • Qin, X., Guo, J., Yuan, C., Chen, C., Hou, J., ...
  • Whittle, D. and Stringer, J., "Improvements in high temperature oxidation ...
  • Sims, C., "The superalloys. Edited by CT Sims and WC ...
  • Seybolt, A. and Beltran, A., "Hot corrosion problems associated with ...
  • Yan, B., Zhang, J., and Lou, L., "Effect of boron ...
  • Decker, R.F. and Freeman, J.W., "The mechanism of beneficial effects ...
  • Qin, X., Guo, J., Yuan, C., Hou, J., and Ye, ...
  • Barbosa, C., Nascimento, J., Caminha, I., and Abud, I., "Microstructural ...
  • Qin, X., Guo, J., Yuan, C., Hou, J., Zhou, L., ...
  • Hardwicke, C.U. and Lau, Y.-C., "Advances in thermal spray coatings ...
  • Juliš, M., Obrtlík, K., Pospíšilová, S., Podrábský, T., and Poláka, ...
  • Davis, J.R., ASM specialty handbook: heat-resistant materials: Asm International, ۱۹۹۷. ...
  • نمایش کامل مراجع