Influence of Multiple Coating and Heat Treatment Cycles on the Performance of Nano-TiO۲ Coating in Protection of ۳۱۶L Stainless Steel against Corrosion under UV Illumination and Dark Conditions
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 115
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-16-2_004
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
In this study nanosized TiO۲coatings on the ۳۱۶L stainless steel substrate were prepared by means of dip-coating technique in which thickness of the coating layer increased byrepeating the coating cycles in two different routes: (I) dipping and drying,respectively, were repeated one, three and five times and finally the dried coated sample was heat treated (single); (II) multiple heat treatment performed after each dipping and drying cycle, respectively.The structural, morphological and optical characterizations of coatings as well as thickness of coatings were systematically studied.The photocatalytic activity of the various TiO۲ coatings was investigated based on the degradation of an aqueous solution of Methyl orange.Moreover, thecorrosion protective properties of coatings were evaluated in both dark and UV illumination conditions based on the obtained polarization curves. The results indicated ۱.۷۵ times improvement in photocatalytic reaction rate constant, a two orders of magnitude decrease in corrosion current density in dark condition and about ۱۴۰ mV electrode potential reduction under UV illumination with optimum coating preparation procedure, repeating the cycle from dipping to heat treatment three times, than the sample prepared with one time coating and heat treatment since this procedure provided not only high thickness and defect-free coating but also transparent one.
کلیدواژه ها:
Nano-TiO۲ coating ، Sol-gel ، Stainless steel ، Multiple coating and heat treatment cycles ، Corrosion protection ، Photoelectrochemical cathodic protection
نویسندگان
M. Karimi Sahnesarayi
Dept. Materials Science & Engineering, Iran University of Science and Technology
H. Sarpoolaky
Dept. Materials Science & Engineering, Iran University of Science and Technology
S. Rastegari
Dept. Materials Science & Engineering Iran University of Science and Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :