Sintering Behavior of Lithium Meta Titanate Nanocrystallites
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 16، شماره: 4
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 198
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-16-4_006
تاریخ نمایه سازی: 1 اسفند 1401
چکیده مقاله:
In this work, lithium meta titanate (Li۲TiO۳) nanocrystallites were synthesized by hydrothermal method and subsequent heat treatment. The shrinkage of the powder compact was measured under constant heating rate in order to study the sintering behavior of the synthesized powders. Densification curves of the synthesized powders were also constructed via the dilatometry analysis and evaluated at several heating rates. Two separate methods of analytical procedure and master curve sintering were employed to determine the activation energy of the initial sintering stage. The activation energy values were estimated based on these two distinct methods as ۲۲۹±۱۴ and ۲۳۰ kJ/mol respectively, consistenting with each other. Moreover, surface diffusion was determined as the dominant mechanism of densification on initial sintering of Li۲TiO۳ nanocrystallites.
کلیدواژه ها:
نویسندگان
A. R. Abbasian
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
M. R. Rahimipour
Ceramic Department, Materials and Energy Research Center, Karaj, ۳۱۷۸۷-۳۱۶, Iran
Z. Hamnabard
Lasers and Optics Research School, NSTRI, Tehran, ۱۱۳۶۵-۸۴۸۶, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :