Diagnosis of AAR in a hydroelectric concrete gravity dam wall and characterisation of the concrete for its rehabilitation

سال انتشار: 1384
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,185

فایل این مقاله در 19 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICCD02_CD5-KN02_3170389354

تاریخ نمایه سازی: 29 مهر 1384

چکیده مقاله:

Signs of concrete distress in a hydroelectric concrete gravity dam in the Snowy Hydro network was noted in routine surveys on the crest of the dam wall and measurement of vertical movements along the crest over a number of years. The distress was also manifested in the form of cracking in some sections of the dam wall. Concrete elements of the associated power station had also shown some degree of distress in the form of cracking. Alkali-aggregate reaction (AAR) was considered among other mechanisms as alikely cause of cracking. In order to investigate the main causes of cracking of the various elements of the power station and the dam wall, core samples ranging in length from 0.3 m to 10 m were extracted and investigated for the presence of AAR, its extent, likelihood of continuing reaction,residual expansion potential, and effect on the strength of concrete. Results of the investigation showed that mild AAR was present in some sections of the wall of the power station but not in the floor, where drying shrinkage could have caused the observed cracking. Mild AAR was also present in sections of the dam wall with minor visible cracking, but it was stronger and more widespread in the badly cracked area. Based on the measurement of the residual expansion, it was suggested that the walls of power station could be treated by appropriate surface coating to mitigate the progress of AAR, and the badly cracked portion of the dam wall be anchored to stabilise the vertical movement. Other portions of the dam wall did not appear to need treatment.

نویسندگان

Ahmad Shayan

Australia

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Shayan, A., Diggins, R.G., Ivanusec, I. and Westgate, P.L. 1988. ...
  • 50 100 150 200 250 300 350 400 Time (days) ...
  • _ 50 100 150 200 250 300 350 _ Time ...
  • نمایش کامل مراجع