Synthesis and Characterization Al۲O۳/Novolac/Fiberglass Nanocomposite: Modification of Thermal Stability and Thermal Insulation Properties
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 245
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-10-1_003
تاریخ نمایه سازی: 11 آبان 1401
چکیده مقاله:
Alumina (Al۲O۳) nanoparticles were used as the additive for modifying a novolac phenolic resin using the solution mixing method. Different weight percentages of nano alumina ۳ and ۸ w% were loaded into the resin, called ۳ARC and ۸ARC nanocomposites, respectively. These nanocomposites were investigated by field emission scanning electron microscopy (FE-SEM), X-ray fluorescence spectroscopy (XRF), energy-dispersive X-ray spectroscopy (EDS), and oxyacetylene flame test (OFT). The FE-SEM images exhibited that at low concentrations (۳ARC), the nano alumina particles were dispersed uniformly on the surface of novolac resin; however, at high concentrations, the dispersion was repressed by aggregation in the nanocomposites. OFT proved that with increasing alumina content in the nanocomposite, the back temperature of the sample decreases and thus improves the thermal insulation properties.
کلیدواژه ها:
نویسندگان
Mohsen Rezaei Qazviniha
Department of Chemistry, Faculty of Sciences, Zanjan University, Zanjan, Iran
Farideh Piri
Department of Chemistry, Faculty of Sciences, Zanjan University, Zanjan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :