Experimental investigation and parameter optimization of Cr۲O۳ atmospheric plasma spray nanocoatings
محل انتشار: فصلنامه سنتز و تفجوشی، دوره: 1، شماره: 3
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 215
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_SYNSINT-1-3_002
تاریخ نمایه سازی: 9 آبان 1401
چکیده مقاله:
In this research, Cr۲O۳ ceramic nano-sized powder particles were prepared using ball milling and then were granulated to reach the proper size for spraying. Afterward, Cr۲O۳ nano-coatings were deposited by atmospheric plasma spraying (APS) process onto stainless steel substrates. To optimize APS parameters, spraying was carried out under six conditions with different parameters. Microstructures of the elemental/milled powder and coatings were characterized via a field emission scanning electron microscope (FESEM) equipped with energy-dispersive spectroscopy (EDS). In this research, Cr۲O۳ coatings were deposited under different spraying conditions to understand the effect of APS parameters on the splat formation, deposition efficiency, and porosities of the coatings. After parameter optimization, spraying was performed under a high deposition efficiency of ۴۶.۰±۱.۳%. The optimized Cr۲O۳ coatings showed porosity content, Knoop microhardness, and adhesive strengths of ۸.۷±۲.۲%, ۸۲۳±۲۷ HK۰.۲, and ۴۹±۴ MPa, respectively; making them a good candidate for industrial use.© ۲۰۲۱ The Authors. Published by Synsint Research Group.
کلیدواژه ها:
نویسندگان
Seyedmahdi Hashemi
Dynamic and Smart Systems Laboratory, Mechanical Industrial and Manufacturing Engineering Department, University of Toledo, OH ۴۳۶۰۶, USA
Nader Parvin
Department of Materials and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Zia Valefi
Materials Engineering Research Center, Malek Ashtar University of Technology, Tehran, Iran
Soroush Parvizi
Materials Engineering Department, Shahid Rajaee Teacher Training University (SRTTU), Tehran, Iran