Mechanical Behavior and Percolation of Pore Space in the Interfacial Transition Zone of Concrete

سال انتشار: 1384
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,340

فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICCD02_CD3-002_4499011942

تاریخ نمایه سازی: 29 مهر 1384

چکیده مقاله:

The cement paste in the interfacial transition zone (ITZ) around aggregate particles has a significantly higher porosity than bulk cement paste. This elevated porosity will effect the transport properties of concrete. The molten metal penetration test was utilized to intruded into voids and fractures in concrete and then solidified to preserve the geometry of the microcracks. The penetration of this alloy, knows as Wood's metal, into concrete samples indicates that the porosity in the interfacial zone is permeated preferentially to the bulk paste. This technique also indicates the width of the interfacial zone in which the porosity is interconnected.

نویسندگان

K. Mostashar Nemati

University of WashingtonSeattle, Washington ۹۸۱۹۵-۱۶۱۰, USA

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Snyder, K.A., Winslow, D.N., Bentz, D.P., and Garboczi, E.J., «Effects ...
  • Bentz, D.P. and Garboczi, E.J., «Percolation of phases in a ...
  • Scrivener, K.L., Patel, H.H., Pratt, P.L. and Parrott, L.J., *Analysis ...
  • Nemati, K.M., Monteiro, P.J.M., and Cook, N.G.W.، A New Method ...
  • Nemati, K.M., Monteiro, P.J.M., and Scrivener, K.L. *Analysis of Compressive ...
  • نمایش کامل مراجع