The Effect of heat treating on nano-structure sheet produced by Accumulative Roll Bonding
محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,662
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICMH03_071
تاریخ نمایه سازی: 21 تیر 1391
چکیده مقاله:
Grain atomizing is an effective and economical method to improve the mechanical properties of materials. Process of Accumulative Roll Bonding (ARB) is a way of sever plastic deformation which used for metallic grain atomizing in sub-micron scale without dimensional changes of sheets. In this study, ARB process was done on AL 5083 sheet in 6 cycles (strain of 4.8), then heat treated in different temperatures. Micro structure changes during ARB and after heat treatment was studied by TEM. In order to analyze the mechanical properties of ARB Aluminum sheets before and after heat treatments, mono-axes tensile test and hardness test was applied. Also, the analysis of fracture surfaces samples after tensile tests was done by SEM. The results show that changes in micro-structure and dislocation collection starts from 100ºC and the maximum differences and changes of micro structure appears on 200ºC. Furthermore, The tensile and hardness test had the same result as well as micro structure analysis. In addition to, fracture surfaces in different temperatures declared an increase in ductile dimples in accordance with heat treating temperature increase. In this case, in order to obtain the ideal strength and elongation the optimum temperature was 120ºC & grain size was measured about 200 NM.
کلیدواژه ها:
نویسندگان
s Akhavan
Prof. in Material Science & Engineering
a Tahvilian
Prof. in Material Science & Engineering
a Saghayannejad
Prof. in Material Science & Engineering
f Ashrafezadeh
Prof. in Material Science & Engineering
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :